DLC HARDENED STEEL NOZZLE

DLC HARDENED STEEL NOZZLE

Wear-resistance, high temperature performance, suitable for 3D printing composites with abrasive additives such as Carbon Fiber, Steel, Wood, Boron Carbide, Tungsten and Phosphorescent pigment as well as conventional filaments.
$30.00 USD
$30.00 USD
Sale Sold out
Model
Nozzle diameter
Filament diameter
View full details

  • 7.8

    Hardness (Mohs)

  • 450℃

    Maximum Printing Temperature

  • 26W/m·k

    Thermal Conductivity

  • 12μm/m·℃

    Expansion Coefficient

Adaptation Models

1100-PS-HS
1200-PS-HS
1110-PH-HS

175：Φ0.10/Φ0.15/Φ0.20/Φ0.25/Φ0.30/Φ0.35/Φ0.40/Φ0.50/Φ0.60/Φ0.80/Φ1.00
300：Φ0.10/Φ0.15/Φ0.20/Φ0.25/Φ0.30/Φ0.35/Φ0.40/Φ0.50/Φ0.60/Φ0.80/Φ1.00

Performance Analysis

DLC coating on whole nozzle surface with its hardness HV2200, thickness 2μm, and friction coefficient 0.05; Fine finish, low adhesion, high wear resistance.Superior quality imported high-speed steel bars, special post-treatment, high temperature hardness up to HRC62.Overall high temperature resistance 450℃, suitable for PEEK and other special engineering plastics printing.Min. hole diameter 0.2mm (±0.01mm) to meet special application requirements and enable high accuracy printing.
Special processing technology and post-treatment ensure fine orifice and high smooth inner hole.

Applicable Filament

Wear-resistance, high temperature performance, suitable for 3D printing composites with abrasive additives such as Carbon Fiber, Steel, Wood, Boron Carbide, Tungsten and Phosphorescent pigment as well as conventional materials.

Product Features

  • φ0.2

    Min. Orifice Diameter

  • ±0.01mm

    Tolerance

  • ≤Ra0.4μm

    Inner Hole Roughness

  • ≤0.02mm

    Concentricity