硬化钢喷嘴

 
7.8

莫氏硬度


450

最高打印温度


22W/m·k

导热系数


8μm/m·℃

热膨胀系数



 
3D打印耗材中,含有碳纤维、钢、木材、碳化硼、钨和磷光颜料等研磨添加剂的复合耗材往往硬度很大。使用普通喷嘴打印,会很快磨损小孔及内径,破坏喷嘴原本性能。
而由硬化钢材质制成的喷嘴莫式硬度7.8 ,最高打印温度450℃,耐磨损、耐高温,是用户打印高强度耗材的首选喷嘴!
超过HRC60硬度将确保磨料的长期打印对喷嘴内孔和平面最小磨损;
耐温度最高可达450℃,可轻松打印PEEK等特种工程塑料;
小于Ra0.4的内孔粗糙度,光洁度更高,粘附力更小;
最小孔径0.1mm( ±0.01mm)实验室级应用,确保高质量的打印;
优质的进口模具钢棒材,保证性能的稳定性。
1100/PHS RepRap M6
1002/PHS MK8
1026/PHS MK10
1025/PHS MK10 PTFE
1110/PHS RepRap M6 Plus
175:Φ0.10/Φ0.15/Φ0.20/Φ0.25/Φ0.30/Φ0.35/Φ0.40/Φ0.50/Φ0.60/Φ0.80/Φ1.00
300:Φ0.10/Φ0.15/Φ0.20/Φ0.25/Φ0.30/Φ0.35/Φ0.40/Φ0.50/Φ0.60/Φ0.80/Φ1.00

Hardness over HRC60 makes an minimum wear at the hole size after a long time printing with abrasive materials.
Temperature resistance up to 450℃, easily handling with special engineering plastics such as PEEK.
Special processing technology and post-treatment make the nozzle without burr at the edge of tip and without debris in the hole.
Inner hole roughness lower than Ra0.4; Higher smoothness and less adhesion.
Min. orifice diameter 0.1mm/±0.01mm in experimental level application, making sure high accuracy printing.
High quality imported die steel material ensures the stability of performance.

适宜于处理
耐磨损、耐高温,适宜于常规耗材之外含有碳纤维、钢、木材、碳化硼、钨和磷光颜料等研磨添加剂的复合耗材的打印。


最小孔径
φ0.10

容差精度
±0.01mm

内孔粗糙度
≤Ra0.4μm

内孔同心度
≤0.02mm