DLC硬化鋼ノズル

	__ __
Description	Description - __
Vendor	Vendor - __
	詳細を見る

Phaetus Store NOZZLE DLC HARDENED STEEL NOZZLE

/

DLC硬化鋼ノズル

$30.00

Shop Now

About this item

耐摩耗性、高温性能を備え、従来のフィラメントだけでなく、炭素繊維、鋼、木材、炭化ホウ素、タングステン、リン光顔料などの研磨添加剤を使用した複合材料の 3D 印刷に適しています。

Authencity Guaranteed

We only sell authentic products from verified brand partners and retail partners globally.

Product specifications

Hardness (Mohs)

7.8

Maximum Printing Temperature

450℃

Thermal Conductivity

26W/m·k

Expansion Coefficient

12μm/m·℃

Adaptation Models

1100-PS-HS
1200-PS-HS
1110-PH-HS

175：Φ0.10/Φ0.15/Φ0.20/Φ0.25/Φ0.30/Φ0.35/Φ0.40/Φ0.50/Φ0.60/Φ0.80/Φ1.00
300：Φ0.10/Φ0.15/Φ0.20/Φ0.25/Φ0.30/Φ0.35/Φ0.40/Φ0.50/Φ0.60/Φ0.80/Φ1.00

Performance Analysis

DLC coating on whole nozzle surface with its hardness HV2200, thickness 2μm, and friction coefficient 0.05; Fine finish, low adhesion, high wear resistance.Superior quality imported high-speed steel bars, special post-treatment, high temperature hardness up to HRC62.Overall high temperature resistance 450℃, suitable for PEEK and other special engineering plastics printing.Min. hole diameter 0.2mm (±0.01mm) to meet special application requirements and enable high accuracy printing.
Special processing technology and post-treatment ensure fine orifice and high smooth inner hole.

Applicable Filament

Wear-resistance, high temperature performance, suitable for 3D printing composites with abrasive additives such as Carbon Fiber, Steel, Wood, Boron Carbide, Tungsten and Phosphorescent pigment as well as conventional materials.

Product Features

Min. Orifice Diameter

φ0.2

Tolerance

±0.01mm

Inner Hole Roughness

≤Ra0.4μm

Concentricity

≤0.02mm