aeWorthy™ ASA-GF

aeWorthy™ ASA-GF is a high-strength ASA type material with excellent mechanical properties. The tensile strength of its 3D printing parts in the XY direction can reach 40MPa. Due to the addition of chopped glass fiber, its anti-warping ability and dimensional stability have been significantly improved, and ASA material has excellent anti-ultraviolet aging performance, which is very suitable for printing large size models and outdoor applications.
aeWorthy™ ASA-GF can work with aeSupport™ S-Multi Quick-Remove Support Material to solve the problem of poor molding effect of complex model support surface.

Color: Beige / Black / Red /Yellow / Orange 

Diameter: 1.75mm / 2.85mm

Net weight: 1kg

Recommended Nozzle:

DLC Hardened Steel Nozzle

Hardened Steel Nozzle

Tungsten Carbide Nozzle

Ruby Nozzle

Recommended Hotend:Dragon series / Dragonfly series

Material Properties

Property Testing method Typical value
Density ISO 1183 1.10g/cm³
Glass transition temperature ISO 11357 98℃
Melt index 250℃,2.16kg 4g/10min
Vicat softening temperature ISO 306 106℃
Determination of temperature

ISO 75:Method A

ISO 75:Method B

90℃ (1.8MPa)

95℃ (0.45MPa)

Tensile breaking strength

ISO 527
45.78 ± 1.08MPa
Elongation at break 3.05 ± 0.18%
Young’s Modulus 2871.68 ± 96.09MPa
Tensile breaking strength

ISO 527
30.86 ± 1.74MPa
Young’s Modulus 2352.06 ± 107.69MPa
Elongation at break 1.76 ± 0.25%
Bending strength
ISO 178
79.59 ± 1.74MPa
Bending Modulus 2751.21 ± 34.44MPa
Charpy impact strength ISO 179 7.08 ± 0.83KJ/㎡

Specimens printed under the following conditions: Nozzle size 0.4mm,Nozzle temp 250°C, Bed temp 100°C, Print speed 50mm/s, Infill 100%, Infill angle ±45°

Recommended printing conditions

Nozzle Temperature250-270℃
Recommended Nozzle Diameter≥0.2 mm
Recommended build surface treatmentGlass、PEI Film or PC Film
Build plate temperature100-110℃
Raft separation distance0.2 mm
Cooling fan speed0%-20%
Print speed30-90 mm/s
Retraction distance1-5 mm
Retraction speed1800-3600 mm/min
Recommended support materialaeSupport™ S-Multi Quick-Remove Support

Other sugggestions:

1.Compared with PLA and PETG filaments, ASA/ABS needs a higher environment temperature to release the residual stress during printing. Please keep the chamber closed to avoid warping and layer separation issues during the process. If your printer has a heated enclosure already, please keep the chamber temperature between 60-80°C.
2.If the ASA-GF filament has been unpacked for a long time and the printing quality starts to degrade during the printing process, please dry the filament at 70-80°C for 4-6 hours before printing.
3.Although aeWorthyTM ASA-GF has much less odor compared with similar products, it is still recommended to place the printer in a well-ventilated area during printing.
4.It is recommended to use hardened steel and above grade nozzles made by Phaetus, which can effectively improve the print quality.

Packing List