Additional Suggestions：

aesupport™ S-Multi very easy to absorb moisture within the environment, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the aesupport™ S-Multi vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.

After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 80-100℃ for 4-6h to restore the printing quality of aesupport™ S-Multi.

It is recommended to use hardened steel and above grade nozzles made by Phaetus, which can effectively improve the print quality. Besides, it is recommended that the thickness of the heating block is longer 12mm.

In dual-extruder printing mode, the material in the standby nozzle will deteriorate due to prolonged heating, and the deteriorated material needs to be squeezed out before the print nozzle is switched, so it is necessary to use the Wipe wall or Wipe tower function in the slicing software.

After the printing is completed, the printed part can be annealed and then the aesupport™ S-Multi removal step can be performed. During the annealing process, aesupport™ S-Multi can play the role of supporting the body material, reducing the dimensional deformation of the body material and improving the mechanical properties of the body material. Annealing conditions: set according to the requirements of the body material.