aeForce™ PETG-ESD
PETG-ESD is a 3D printing material with anti-static properties, as well as good printability and balanced mechanical performance.
Color: Black
Diameter: 1.75mm / 2.85mm
Net weight: 1kg / 3kg
Recommended Nozzle：
DLC Hardened Steel Nozzle
Hardened Steel Nozzle
Ruby Nozzle
Recommended Hotend：Dragon series / Dragonfly series
Material Properties
| Property | Testing method | Typical value |
| Density | ISO 1183 | 1.24 g/cm³ |
| Glass transition temperature | ISO 11357 | 78℃ |
| Melt index | 230℃，2.16kg | 3.6g/10min |
| Determination of temperature | ISO 75：Method A ISO 75：Method B | 68℃ (1.8MPa) 70℃ (0.45MPa) |
| Surface resistivity | ANSI ESD S11.11 | 106Ω（per square） |
| Solume resistivity | ANSI ESD S11.12 | 106Ω.m |
| Young’s Modulus(X-Y) | ISO 527 | 1550±118MPa |
| Tensile strength(X-Y) | 30±0.8 MPa | |
| Elongation at break(X-Y) | 5.1±0.2% | |
| Tensile strength(Z) | ISO 527 | 1.91±0.3% |
| Elongation at break(Z) | 26.9±1.8MPa | |
| Young’s Modulus(Z) | 1950±208MPa | |
| Bending strength(X-Y) | ISO 178 | 55.8±1.8MPa |
| Bending Modulus(X-Y) | 1890±189 MPa | |
| Charpy impact strength | ISO 179 | 8.9±0.9 KJ/㎡ |
Recommended printing conditions
| Nozzle Temperature | 250-280℃ |
| Recommended Nozzle Diameter | 0.2-1.0mm |
| Recommended build surface treatment | Glass、PEI Film or Coating with PVP glue |
| Build plate temperature | 70-80℃ |
| Raft separation distance | 0.18-0.25 mm |
| Cooling fan speed | ≤50% |
| Print speed | 30-60 mm/s |
| Retraction distance | 2-5 mm |
| Retraction speed | 1800-2400 mm/min |
| Recommended support material | aeSupport™ S-Multi Quick-Remove Support |
Other sugggestions： The surface resistivity of PETG-ESD components is largely affected by print quality, and when the surface resistivity is too high, it is recommended to increase the printing temperature or extrusion rate. | |
Packing List
- Materials
- Packing
- Instructions
- Aluminum foil bag