aeFlex™ TPU-95A-HF
aeFlex™ TPU-95A-HF is TPU material that is easy to print. aeFlex™ TPU-95A-HF is easier to be extruded than other conventional TPU consumables under the same hardness. When a suitable extruder is selected, aeFlex™ TPU-95A-HF can support a printing speed of more than 100mm/s.
Color: Transparent / White / Black / Blue / Orange
Diameter: 1.75mm / 2.85mm
Net weight: 1kg
Recommended Nozzle：
DLC Hardened Steel Nozzle
Hardened Steel Nozzle
Ruby Nozzle
Recommended Hotend：Dragon series / Dragonfly series
Material Properties
| Property | Testing method | Typical value |
| Density | ISO 1183 | 1.15g/cm³ |
| Hardness | ISO 7619 | 95A |
| Melt index | 200℃，2.16kg | 30g/10min |
| Vicat softening temperature | ISO 306 | 99℃ |
| Tensile breaking strength (X-Y) | ISO 527 | 31.81±3.26MPa |
| Elongation at break (X-Y) | 471±81% | |
| Tensile stress at 100% (X-Y) | 9.75±0.16MPa | |
| Tensile stress at 200% (X-Y) | 12.2±0.27MPa | |
| Tensile stress at 300% (X-Y) | 17.0±0.49MPa |
Recommended printing conditions
| Nozzle Temperature | 210-230℃ |
| Recommended Nozzle Diameter | ≥0.2mm |
| Recommended build surface treatment | Glass, PEI Film or PC Film |
| Build plate temperature | 20-50℃ |
| Raft separation distance | 0.18-0.22mm |
| Cooling fan speed | On |
| Print speed | 30-120 mm/s |
| Retraction distance | 1-5 mm |
| Retraction speed | 1800-3600 mm/min |
|
Other sugggestions： If you want to achieve high-speed printing, it is recommended to use direct extruders, such as BMG extruder, Titan extruder and Hemera extruder, and appropriately increase the nozzle temperature. TPU material is very easy to absorb moisture when exposed to air, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the eFlex™ TPU-95A vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage. After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 70-80℃ for 4-6h to restore the printing quality of aeFlex™ TPU-95A-HF. |
|
Packing List
- Materials
- Packing
- Instructions
- Aluminum foil bag