aeFlex™ TPU-78D

aeFlex™ TPU-78D is a high hardness TPU 3D printing material, higher surface hardness and modulus greatly reduce the TPU in the printing process because of too soft to jam the extruder, improve the success rate of printing.

Color: Black/White

Diameter: 1.75mm / 2.85mm

Net weight: 1kg

Recommended Nozzle:

DLC Hardened Steel Nozzle 1100-HSD

Hardened Steel Nozzle 1100-HS

Ruby Nozzle A019

Recommended Hotend:Dragon series / Dragonfly series

Material Properties

Property Testing method Typical value
Density ISO 1183 1.24 g/cm³
Glass transition temperature ISO 11357 78℃
Melt index 220℃,2.16kg 13.2 g/10min
Vicat softening temperature ISO 306 122°C
Tensile breaking strength(X-Y) ISO 527 36.55±2.11MPa
Young’s Modulus 1026.21±220.80MPa
Elongation at break (X-Y) 237.38±13.49%
Tensile stress at 100% (X-Y) 28.81±0.42MPa
Tensile stress at 200% (X-Y) 33.81±1.05MPa
Bending strength(X-Y) ISO 178 18.91±0.29MPa
Bending modulus(X-Y) 532.07±46.37MPa

Recommended printing conditions

Nozzle Temperature 210-230℃
Recommended Nozzle Diameter ≥0.2mm
Recommended build surface treatment Glass, PEI Film or PC Film
Build plate temperature 50-70°C
Raft separation distance 0.18-0.22 mm
Cooling fan speed On
Print speed 30-120 mm/s
Retraction distance 1-5 mm
Retraction speed 1800-3600 mm/min
Recommended support material /

Other sugggestions:

TPU material is very easy to absorb moisture when exposed to air, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the aeFlex™ TPU-78D vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.

After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 70-80°C for 4-6h to restore the printing quality of aeFlex™ TPU-78D.