aeCoating™ NexPA-CF25 is an outstanding candidate for printing parts that need to have thin walls and high mechanical property requirements. It is one type of 3D printing filament with 25% carbon fiber content and a skin-core structure. The outer ‘skin’ of the filament is a modified resin with high layer adhesion strength, and the inner core is reinforced resin containing high chopped fiber content. aeCoating™ 3D printing filaments take advantage of the general laminar flow of polymeric fluids during extrusion and maintain the stable skin-core structure even after the filament passes through the nozzle of the printer. This technology contributes to the excellent Z-axis interlayer adhesion of FDM fiber-reinforced filaments because the major layer adhesion comes from the outer shell rein without fibers. Meanwhile, 25% chopped cabron fiber content can improve the mechanical properties and heat resistance of the printed parts.
Diameter: 1.75mm / 2.85mm
Net weight: 500g / 1kg / 2.5kg
DLC Hardened Steel Nozzle 1100-HSD
Hardened Steel Nozzle 1100-HS
Ruby Nozzle A019
Recommended Hotend：Dragon series / Dragonfly series
|Property||Testing Method||Typical Value|
|ISO 1183||1.23 g/cm³|
|ISO 62:Method 1||0.5%|
|Determination of temperature||ISO 75: Method A||122.5 °C (1.80MPa)|
|ISO 75: Method B||187.5°C (0.45MPa)|
|ISO 527||103.25 ± 2.96 Mpa|
|Young’s modulus(X-Y)||8789.10 ± 458.32 Mpa|
|Elongation at break (X-Y)||1.49±0.09 %|
|Bending strength (X-Y)||ISO 178||170.09±4.88 Mpa|
|Bending modulus (X-Y)||8568.60±172.79 Mpa|
|Charpy impact strength （X-Y）||ISO 179||6.57±0.38 KJ/㎡|
|Tensile strength (Z)||ISO 527||51.51±2.01 MPa|
|Young’s modulus (Z)||4213.96±87.46 MPa|
|Elongation at break (Z)||1.55±0.12 %|
Recommended printing conditions
|Recommended Nozzle Diameter||0.4-1.0mm|
|Recommended build surface treatment||PEI or Coating with PVP glue|
|Build plate temperature||70-80℃|
|Raft separation distance||0.08-0.12 mm|
|Cooling fan speed||Off|
|Print speed||30-90 mm/s|
|Retraction distance||1-3 mm|
|Retraction speed||1800-3600 mm/min|
|Recommended support material||aeSupport™ S-PAHT Quick-Remove Support|
Nylon material is very easy to absorb moisture within the environment, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the aeCoating™ NexPA-CF25 vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.
After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 80-100°C for 4-6h to restore the printing quality of aeCoating™ NexPA-CF25.
It is recommended to use hardened steel and above grade nozzles made by Phaetus, which can effectively improve the print quality. Besides, it is recommended that the thickness of the heating block is longer 12mm.
After the printing is completed, the aeCoating™ NexPA-CF25 printed part can be annealed to further improve the strength of print part. Annealing conditions: leave printing part in an oven at 80-100°C for 4 to 8 hours and cool to room temperature naturally.
Extrusion Force vs Print Speed Test
Test parameters: 12mm length brass heat block, BMG extruder, Phaetus Hardened Steel Nozzle, Nozzle size 0.4mm, Layer Height 0.2mm.